Bambu PC White with Bambu Reusable Spool 1.75mm 3D Printer Filament 1kg/Roll
Bambu PC material in white colour 3D Printer Filament, Dimensional Accuracy 1.75mm, 1kg(2.2lbs) with reusable Spool 3D Printing Filament Fits for Bambulab X1 Carbon, X1E FDM 3D Printers. This High quality PC Filament available at electrobes has weight of 1Kg.
₨ 24,000
Bambu PC White with Bambu Lab Reusable Spool 1.75mm 3D Printer Filament 1kg/Roll
Product Features:
- Exceptional Thermal Resistance
- Excellent Mechanical Properties
- High Impact Strength and Durability
- Suitable for Engineering Purpose
- Comes with High Temperature Reusable Spool
- Diameter: 1.75mm +/- 0.03mm
Cautions for Use
- Dry out before use
- AMS Compatible
- AMS lite NOT Compatible
- Enclosure Printers Required
| Recommended | Not Recommended | |
| Build Plate | Engineering Plate, High Temperature Plate or Textured PEI Plate | Cool Plate |
| Hotend | All Size / Material | / |
| Glue | Glue Stick | Bambu Liquid Glue |
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Load and print! No more tedious setting steps.
| Recommended Printing Settings | |
| Drying Settings (Blast Drying Oven) | 80 °C，8h |
| Printing and Keeping Container’s Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 250 – 270 °C |
| Bed Temperature (with Glue) | 90 – 110 °C |
| Printing Speed | < 300 mm/s |
| Physical Properties | |
| Density | 1.20 g/cm³ |
| Vicat Softening Temperature | 119 °C |
| Heat Deflection Temperature | 117 °C |
| Melting Temperature | 228 °C |
| Melt Index | 32.2 ± 2.9 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 55 ± 4 MPa |
| Breaking Elongation Rate | 3.8 ± 0.3 % |
| Bending Modulus | 2310 ± 70 MPa |
| Bending Strength | 108 ± 4 MPa |
| Impact Strength | 34.8 ± 2.1 kJ/m² |
- Dimensions: 195 x 73 mm
- Filament diameter: 1.75 mm
- Weight (Kg): 1 Kg
- Thickness: 1.24 g/cm3
- Density: 1.20 g/cm³
- Vicat Softening Temperature: 119 °C
- Heat Deflection Temperature: 117 °C
- Melting Temperature: 228 °C
- Melt Index: 32.2 ± 2.9 g/10 min